公司基本資料信息
|
|||||||||||||||||||||||||||
|
項目
|
測試方法
|
指標
|
|
絕緣內層
|
||
|
拉伸強度
|
ASTM D2671
|
≥5MPa
|
|
斷裂伸長率
|
ASTM D2671
|
≥800%
|
|
密度
|
ASTM D792
|
1.0g/cm3
|
|
擊穿強度
|
IEC243
|
≥29kV/mm
|
|
體積電阻率
|
IEC93
|
≥1015Ω.cm
|
|
吸水率
|
ISO 62/23℃,14days
|
<0.15%
|
|
半導外層
|
||
|
拉伸強度
|
ASTM D638
|
≥13MPa
|
|
斷裂伸長率
|
ASTM D638
|
≥400%
|
|
密度
|
ASTM D792
|
1.10g/cm3
|
|
體積電阻率
|
IEC93
|
≤104Ω.cm
|
|
吸水率
|
ISO 62/23℃,14days
|
<0.15%
|
|
規格
(mm)
|
擴張尺寸（最小）
|
收縮后尺寸(mm)
|
標準長度
(mm)
|
||
|
內徑
|
總壁厚
|
外導電層壁厚
|
|||
|
XEDT-100
|
|||||
|
XEDT-100 35/13
|
40
|
13
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 45/17
|
48
|
17
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 50/21
|
56
|
21
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 65/26
|
65
|
26
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 70/30
|
75
|
30
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 80/36
|
85
|
36
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 90/40
|
95
|
40
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-100 120/50
|
125
|
50
|
7.80±0.40
|
0.80±0.10
|
1000
|
|
XEDT-360
|
|||||
|
XEDT-360 35/13
|
37
|
13
|
11.0
|
0.80±0.10
|
1000
|
|
XEDT-360 46/17
|
46
|
17
|
12.0
|
0.80±0.10
|
1000
|
|
XEDT-360 56/21
|
56
|
21
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 66/26
|
66
|
26
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 82/26
|
82
|
26
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 78/34
|
78
|
34
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 88/34
|
88
|
34
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 95/42
|
95
|
42
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 115/53
|
115
|
53
|
13.5
|
0.80±0.10
|
1000
|
|
XEDT-360 125/62
|
125
|
62
|
14.0
|
0.80±0.10
|
1000
|